国外阀门材料常用技术标准 需切口韧性试验的管道部件用碳钢和低合金钢锻件、化学成分要求

元素	成分，（重量）%
	LF1	LF2	LF3	LF5	LF6	LF9	LF787
碳 C≤	0.30	0.30	0.20	0.30	0.22	0.20	0.07
锰 Mn	0.60-1.35	0.60-1.35	≤0.90	0.60-1.35	1.15-1.50	0.40-1.06	0.40-0.70
磷 P≤	0.035	0.035	0.035	0.035	0.025	0.035	0.025
硫 S≤	0.040	0.040	0.040	0.040	0.025	0.040	0.025
硅 SiA	0.15-0.30	0.15-0.30	0.20-0.35	0.20-0.35	0.15-0.30	…	≤0.40
镍 Ni	≤0.40B	≤0.40B	3.3-3.7	1.0-2.0	≤0.40B	1.60-2.24	0.70-1.00
铬 Cr	≤0.30B,C	≤0.30B,C	≤0.30C	≤0.30C	≤0.30B,C	≤0.30C	0.60-0.90
钼 Mo	≤0.12B,C	≤0.12B,C	≤0.12C	≤0.12C	≤0.12B,C	≤0.12C	0.15-0.25
铜 Cu	≤0.40B	≤0.40B	≤0.40	≤0.40C	≤0.40B	0.75-1.25	1.00-1.30
铌 Nb	≤0.02D	≤0.02D	≤0.02	≤0.02	≤0.02	≤0.02	≥0.02
钒 V	≤0.08	≤0.08	≤0.03	≤0.03	0.04-0.11	≤0.03	≤0.03
氮 N	…	…	…	…	0.01-0.030	…	…